University of Hertfordshire

  • Wang Shaoquan
  • Dong Shangli
  • Gao Yu
  • Togay Ozbakkaloglu
View graph of relations
Original languageEnglish
Number of pages11
Pages (from-to)235-245
JournalComposites Part A: Applied Science and Manufacturing
Journal publication date1 Apr 2019
Volume119
Early online date4 Feb 2019
DOIs
Publication statusPublished - 1 Apr 2019

Abstract

The effects of vacuum-thermal cycling and hygro-thermal cycling on the fiber/matrix interface characteristics of a carbon fiber reinforced bismaleimide (C/BMI) composite were investigated to assess the degradation behavior of the mechanical property of C/BMI composite in low earth orbit (LEO) and atmosphere environment. The feasibility of using one comprehensive accelerated test procedure capable of representing the LEO and atmosphere environmental effects simultaneously for the aerospace plane was explored for the first time. A simplified mathematical approach and the corresponding model was supplied firstly to prove the reliability and effectiveness of the widely-used SEM observation method in the assessment of fiber matrix interface properties. The dominating degradation mechanism of the C/BMI composites caused by vacuum-thermal cycling in LEO environment is the interfacial sliding induced by thermal stress, whereas the thermal oxidation and decomposition of the matrix is the main degradation mechanism after hygro-thermal cycling in atmosphere environment. Candidate composite materials for aerospace plane must be tested in atmosphere and LEO environments separately in the environmental simulation experiments before their application.

Notes

© 2019 Elsevier Ltd. All rights reserved.

ID: 16534170