Fatigue failure modes in self-piercing riveted aluminium alloy joints

Keyphrases

• 5754 Aluminum Alloy 50%
• Aluminum Alloy Joint 100%
• Aluminum Alloy Sheet 50%
• Applied Load 50%
• Automotive Industry 50%
• Cyclic Loading 50%
• Early-type 50%
• Failure Pattern 50%
• Fatigue Behavior 100%
• Fatigue Failure 50%
• Fatigue Failure Mode 100%
• Fatigue Mechanism 50%
• Infant Mortality 50%
• Interfacial Conditions 50%
• Joining Method 50%
• Piercing 100%
• Public Domain 50%
• Riveted Joints 50%
• Self-piercing Riveted Joint 50%
• Self-piercing Riveting 100%
• Sheet Fracture 50%
• Spot Welding 50%
• Static Test 50%
• Surface Condition 50%
• Three-parameter Weibull Distribution 50%
• Wearout 50%
• Weibull 50%
• Weibull Analysis 50%

Material Science

• Alloy 50%
• Aluminum 50%
• Aluminum Alloy 100%
• Failure Mechanism 50%
• Fatigue Behavior 100%
• Riveted Joint 50%
• Spot Welding 50%